PVC-waterproof-big

PVC Waterproofing Membrane

PVC Waterproofing Membrane

S ulong PVC waterproofing membrane is a new polymer waterproofing membrane, which is made of high quality flexible (plasticized) polyvinyl-chloride. It has advantage of good elasticity, high ductility, little contraction ratio, good flexibility under low temperature, anti-aging and long service life etc


ASK FOR QUOTE pdf-icon    

Product Details

  • Introduction:
    PVC waterproofing membrane is a new polymer waterproof membrane which is made from polyvinyl chloride resin, and mixed with plasticize, filler, anti-oxygen, ultraviolet absorbed and other auxiliaries.
  • Specification:

    Length

    20m/roll or customized
    Width 2m, 3m
    Thickness 1.2mm; 1.5mm; 2.0mm
    Type Homogeneous, Reinforced, Fabric back
    If Exposed Exposed and Non-exposed
    Color White, Yellow, Grey, Black

  • Applications:
    1. All kinds of roofs, such as steel structure roof, planted roof etc;
    2. Underground engineering, such as building basement, subways, tunnels, air raid shelter, etc;
    3. Other projects like artificial lake, dam, water reservoir, grain storehouse, etc;

  • Features:
    1. Excellent aging resistance. Service life of roofing material is over 20 years; service life of underground material is over 50 years.
    2. Root resistant penetration, specially used on planting roof.
    3. Welding installation. Joints are solid and environment friendly, no pollution.
    4. High tensile strength, good elongation and dimensional stability.
    5. Good plasticity, easy and suitable for details installation.
    6. Fireproof. Fire extinguished out of the ignition resource.
    7. Surface is smooth, no fading and dirty resistant.

  • Packaging & Delivery:
    Packaging Detail: Be packed in rolls with plastic belts, film bag,or as required.
    Delivery Detail: 15-20 working days to our port

No.

Items Result
1 Tensile strength, N/cm Longitudinal 214
Transverse 209
2 Elongation at break, %≥ Longitudinal 321
Transverse 317
3 Dimensional changes after Longitudinal 0.4
heat treatment Transverse 0.3
4 Water impermeability (0.3Mpa 24h) qualified
5 Flexibility at low temperatures/°C -25°C scale No cracks
6 Puncture resistance no permeation
7 Adhesivity under shearing, N/mm 5.2
8 Heating ageing treatment appearance No bubble,cracks,hole
change rate of tension, % —7.0 Longitudinal
—8.1 Transverse
change rate of elongation at break, % 2 Longitudinal
5 Transverse
Flexibility at low temperatures No cracks
9 Chemical resistant change rate of tension, % —3 Longitudinal
—3 Transverse
(plumbite treatment) change rate of elongation at break, % 5 Longitudinal
6 Transverse
Flexibility at low temperatures No cracks
10 Chemical resistant change rate of tension, % —1 Longitudinal
—2 Transverse
(alkali treatment) change rate of elongation at break, % 2 Longitudinal
4 Transverse
Flexibility at low temperatures No cracks
11 Chemical resistant change rate of tension, % —1 Longitudinal
2 Transverse
(acid treatment) change rate of elongation at break, % 7 Longitudinal
5 Transverse
Flexibility at low temperatures No cracks
12 Artificial weathering test change rate of tension, % 2 Longitudinal
2 Transverse
change rate of elongation at break, % —1 Longitudinal
—1 Transverse
Flexibility at low temperatures No cracks

Products You Might Like

fabric-air-duct_250

PVC Ventilation Tube Fabrics

ventilation duct-02

Lay Flat Ventilation Duct

ventilation duct-01

Spiral Ventilation Ducting

PVC Truck Tarpaulin

Tarpaulin for Logistics